Exploring meso-/microporous composite molecular sieves with core-shell structures
Exploring meso-/microporous composite molecular sieves with core-shell structures
 
الموضوع : كيمياء 
لغة الوثيقة : الانجليزية 
المستخلص : A series of core-shell-structured composite molecular sieves comprising zeolite single crystals (i.e., ZSM-5) as a core and ordered mesoporous silica as a shell were synthesized by means of a surfactant-directed sol-gel process in basic medium by using cetyltrimethylammonium bromide (CTAB) as a template and tetraethylorthosilicate (TEOS) as silica precursor. Through this coating method, uniform mesoporous silica shells closely grow around the anisotropic zeolite single crystals, the shell thickness of which can easily be tuned in the range of 15-100 nm by changing the ratio of TEOS/zeolite. The obtained composite molecular sieves have compact meso-/micropore junctions that form a hierarchical pore structure from ordered mesopore channels (2.4-3.0 nm in diameter) to zeolite micropores (≈0.51 nm). The short-time kinetic diffusion efficiency of benzene molecules within pristine ZSM-5 (≈7.88×10 -19 m 2s -1) is almost retainable after covering with 75 nm-thick mesoporous silica shells (≈7.25×10 -19 m 2s -1), which reflects the greatly opened junctions between closely connected mesopores (shell) and micropores (core). The core-shell composite shows greatly enhanced adsorption capacity (≈1.35 mmolg -1) for large molecules such as 1,3,5-triisopropylbenzene relative to that of pristine ZSM-5 (≈0.4 mmolg -1) owing to the mesoporous silica shells. When Al species are introduced during the coating process, the core-shell composite molecular sieves demonstrate a graded acidity distribution from weak acidity of mesopores (predominant Lewis acid sites) to accessible strong acidity of zeolite cores (Lewis and BrÃ?nsted acid sites). The probe catalytic cracking reaction of n-dodecane shows the superiority of the unique core-shell structure over pristine ZSM-5. Insight into the core-shell composite structure with hierarchical pore and graded acidity distribution show great potential for petroleum catalytic processes. Esprit de core: Meso-/microporous core-shell composite molecular sieves with hierarchical pore structures (see figure), from opened mesopore channels (2.4-3.0 nm) to accessible micropores (≈0.51 nm), and graded acidity distributions, from weakly acidic mesopores to accessible strongly acidic ZSM-5 cores, have been synthesized. 
ردمد : 0947-6539 
اسم الدورية : Chemistry - A European Journal 
المجلد : 18 
العدد : 3 
سنة النشر : 1433 هـ
2012 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, March 4, 2012 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
Xufang F QianQian, Xufang Fباحثدكتوراه 
Bin LiLi, Bin باحثدكتوراه 
Yuanyuan Y HuHu, Yuanyuan Yباحثدكتوراه 
Guoxing NiuNiu, Guoxing باحثدكتوراه 
Dier ZhangZhang, Dier باحثدكتوراه 
RenChao CheChe, RenChao باحثدكتوراه 
Yi TangTang, Yi باحثدكتوراه 
Dangsheng S SuSu, Dangsheng Sباحثدكتوراه 
عبدالله محمد عسيريAsiri, Abdullah Mohamedباحثدكتوراهaasiri2@kau.edu.sa
Dongyuan ZhaoZhao, Dongyuan باحثدكتوراهdyzhao@fudan.edu.cn

الملفات

اسم الملفالنوعالوصف
 32525.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث